The invention discloses a copper tungsten polishing agent, to the quality of a meter, comprises the following raw materials: Sanya 11 amino methyl phosphonic acid 19, sodium laurate 6 10 copies, 20 copies, 15 triethanolamine glycerol 25 30 copies, 70 copies of 55 deionized water. Using the method of copper tungsten polishing agent and the specific as follows: 1) the Sanya amino methyl phosphonic acid, sodium laurate, triethanolamine, glycerol in deionized water, the temperature is 45 50 DEG C, stirring evenly; 2) to treat copper tungsten steel surface of sandpaper and sandblasting; 3) will step 1) Polish copper processing into pieces of tungsten steel cooling to 45 50 DEG C, in the time of 40 60min; 4) the copper tungsten piece out and cooling immediately after cleaning.
【技術實現步驟摘要】
本專利技術涉及金屬表面處理
，具體涉及鍍銅鎢鋼拋光劑及其使用方法。
技術介紹
金屬表面拋光因能降低金屬制品表面粗糙度，具有增加金屬制品光澤度和消除銹跡等優點，但現有用于鍍銅鎢鋼件的拋光劑產品存在抗腐蝕性能差，穩定性差等問題。
技術實現思路
本專利技術的目的是為了解決現有技術的不足，提供一種鍍銅鎢鋼拋光劑及其使用方法，制得的拋光劑尤其適用于鍍銅鎢鋼，抗抗腐蝕性能強，穩定性好。本專利技術采用如下技術方案：一種鍍銅鎢鋼拋光劑，以質量份計，包括如下原料：氨基三亞甲基膦酸11-19份、月桂酸鈉6-10份、三乙醇胺15-20份、丙三醇25-30份、去離子水55-70份。所述的鍍銅鎢鋼拋光劑的使用方法具體為：1）將氨基三亞甲基膦酸、月桂酸鈉、三乙醇胺、丙三醇依次加入去離子水中，溫度為45-50℃，攪拌均勻；2）將待處理的鍍銅鎢鋼件表面進行砂紙磨平和噴砂處理；3）將步驟1）處理的鍍銅鎢鋼件放入冷卻至45-50℃的拋光劑中，放入時間為40-60min；4）將鍍銅鎢鋼件取出，降溫清洗后即可。本專利技術的有益效果為：本專利技術拋光劑不僅能夠有效的去除鍍銅鎢鋼表面的油污和銹斑，使其表面光澤明亮，而且本專利技術各組分能夠有效配合提高鍍銅鎢鋼件的抗腐蝕性能。具體實施方式下面結合實施例對本專利技術作進一步的詳細描述。實施例1一種鍍銅鎢鋼拋光劑，以質量份計，包括如下原料：氨基三亞甲基膦酸18份、月桂酸鈉8份、三乙醇胺16份、丙三醇28份、去離子水60份。所述的鍍銅鎢鋼拋光劑的使用方法具體為：1）將氨基三亞甲基膦酸、月桂酸鈉、三乙醇胺、丙三醇依次加入去離子水中，溫度為45-50℃，攪拌...
【技術保護點】
一種鍍銅鎢鋼拋光劑，其特征在于，以質量份計，包括如下原料：氨基三亞甲基膦酸11?19份、月桂酸鈉6?10份、三乙醇胺15?20份、丙三醇25?30份、去離子水55?70份。
【技術特征摘要】
1.一種鍍銅鎢鋼拋光劑，其特征在于，以質量份計，包括如下原料：氨基三亞甲基膦酸11-19份、月桂酸鈉6-10份、三乙醇胺15-20份、丙三醇25-30份、去離子水55-70份。2.根據權利要求1所述的鍍銅鎢鋼拋光劑的使用方法，其特征在于：1）將氨基三亞甲基膦酸...