The invention discloses an active carbon powder used for friction material, which is mainly made up of 10 parts of the following parts: 80 to 90 parts of the corn stalk powder, mica powder of between 5 and 10 parts, and molybdenum disulfide to be divided into 5 parts. The corn stalk carbon powder is a carbon powder which is obtained after the corn stalk is washed, dried, crushed and pressed into blocks, carbonized and graphitized. The invention makes full use of corn by-products corn stalk, the carbonization and graphitization, made of activated carbon, as a substitute for natural graphite powder added to the friction material, friction material can effectively reduce the production cost, expand the channels of corn stalk, corn stalk to improve economic benefit.
【技術實現步驟摘要】
本專利技術涉及一種摩擦材料用的活性碳粉。
技術介紹
玉米（拉丁學名：ZeamaysL.）是禾本科玉蜀黍屬一年生草本植物。別名：玉蜀黍、棒子、包谷、包米、包粟、玉茭、苞米、珍珠米、苞蘆、大蘆粟，東北遼寧話稱珍珠粒，潮州話稱薏米仁，粵語稱為粟米，閩南語稱作番麥。稈直立，通常不分枝，基部各節具氣生支柱根。葉鞘具橫脈；葉舌膜質，葉片扁平寬大，線狀披針形，基部圓形呈耳狀，無毛或具疵柔毛，中脈粗壯。穎果球形或扁球形，成熟后露出穎片和稃片之外，其大小隨生長條件不同產生差異。雌雄同株異花，花果期秋季。我國玉米的栽培歷史大約有470多年。目前我國播種面積在3億畝左右，僅次于稻、麥，在糧食作物中居第三位，在世界上僅次于美國。全世界熱帶和溫帶地區廣泛種植，為一重要谷物。收獲玉米之后，會產生大量的副產物---玉米稈。通常人們處理方式是直接焚燒，這種方式雖然對其進行了一定利用，但是焚燒產生的煙塵大，在一定程度上污染環境。目前，隨著工業化的發展，摩擦材料的使用量越來越大，其填料---石墨的使用量也是逐年增加。然而天然石墨的價格還是較高的，而玉米稈中含有大量碳源，如果采用玉米稈制成的碳粉取代石墨添加到摩擦材料中，將極大的降低了摩擦材料的生產成本。
技術實現思路
本專利技術的目的在于提供一種摩擦材料用的活性碳粉。本專利技術充分利用了玉米的副產物---玉米稈，將其進行碳化、石墨化，制成活性碳粉，作為天然石墨粉的替代品加入到摩擦材料中，有效降低了摩擦材料的生產成本，拓寬玉米稈的利用渠道，提高了玉米稈的經濟效益。為了實現上述目的，本專利技術采用了以下技術方案：一種摩擦材料用的活性碳粉，主要由以下...
【技術保護點】
一種摩擦材料用的活性碳粉，其特征在于，主要由以下重量份數的組分配制而成：玉米稈碳粉80～90份、云母粉5～10份和二硫化鉬5～10份。
【技術特征摘要】
1.一種摩擦材料用的活性碳粉，其特征在于，主要由以下重量份數的組分配制而成：玉米稈碳粉80～90份、云母粉5～10份和二硫化鉬5～10份。2.根據權利要求1所述的摩擦材料用的活性碳粉，其特征在于，主要由以下重量份數的組分配制而成：玉米稈碳粉85份、云母粉8份和二硫化鉬7份。3.根據權利要求1或2所述的摩擦材料用的活性碳粉，其特征在于：所述的玉米稈碳粉是將玉米稈依次經清洗烘干、粉碎壓制成塊、碳化處理、石墨化處理之后獲得的碳粉末。4.權利要求3所述的摩擦材料用的活性碳粉，其特征在于，所述的碳化處理具體為：將玉米稈塊放入貧氧爐進行碳化處理；排潮期從點火至爐溫上升到150℃，時間為5小時；然后升溫至250℃，打開鼓風機，對爐內鼓...
【專利技術屬性】
技術研發人員：盧怡臻，
申請(專利權)人：廣西南寧勝祺安科技開發有限公司，