Manufacturing method of a ceramic scratch repairing agent, relates to a production method of repair agent, the method comprises the following steps: (1) the concentration of dilute phosphoric acid, the concentration of 20% to 40% of hydrofluoric acid in the ratio of 1: 0.30 to 0.43 are mixed, the mixture solution is dripped on the ordinary ceramic surface to be repaired and stay for 1 to 2 minutes; (2) the concentration of hydrofluoric acid and 40% alumina powder in the weight ratio of 1 to 0.75 are mixed, evenly stirred, get white paste, add it to the dilute phosphoric acid and hydrofluoric acid ceramic surface treatment, after 5 to 10 hours to complete paste after solidification polished ceramic surface damage can be repaired. The repair agent can quickly repair the ceramic surface damage without polluting the environment.
【技術實現步驟摘要】
本專利技術涉及一種修復劑的制作方法，特別是涉及一種陶瓷劃痕 修復劑的制作方法。技術背景陶瓷制品盡管硬度很高，但是由于往往暴露在環境之中，所以很 容易出現劃痕，劃痕出現后由于對光線不均勻反射，會影響陶瓷制品 的外觀。現有的劃痕修復劑對陶瓷的修復均不能達到理想效果。
技術實現思路
本專利技術的目的在于提供一種以稀磷酸、氫氟酸和氧化鋁為主要原 料的陶瓷修復劑。本專利技術的目的是通過以下技術方案實現的 ，該方法包括如下步驟(1) 將濃度為20%的稀磷酸、濃度為40%的氫氟酸按質量比1 :0.30 0.43混合，將該混合物溶液滴加在需修復的普通陶瓷表面并停留1 2分鐘；(2) 將濃度為40%的氫氟酸與氧化鋁粉末按質量比1: 0.75混合， 攪拌均勻，得到白色膏狀物，將其添加到經稀磷酸和氫氟酸處理過的 陶瓷表面，經5 10小時待膏體完全凝固后，拋光，陶瓷表面的損傷 即可得到修復。如上所述的，所述的稀磷酸、氫氟酸和氧化鋁均為工業級產品。 本專利技術的優點與效果是本專利技術的陶瓷修復劑以稀磷酸、氫氟酸和氧化鋁為主要原料，其 可快速對陶瓷表面的損傷進行修復，并且不會對環境造成污染。具體實施方式實施例l將濃度為20%的稀磷酸、濃度為40%的氫氟酸按質量比1: 0.30混 合，將該混合物溶液滴加在需修復的普通陶瓷表面并停留2分鐘；將 濃度為40%的氫氟酸與氧化鋁粉末按質量比1: 0.75混合，攪拌均勻， 得到白色膏狀物，將其添加到經稀磷酸和氫氟酸處理過的陶瓷表面， 經5 10小時待膏體完全凝固后，拋光，陶瓷表面的損傷即可得到修 復。實施例2將濃度為20%的稀磷酸、濃度為40...
【技術保護點】
一種陶瓷劃痕修復劑的制作方法，其特征在于，該方法包括如下步驟：（１）將濃度為２０％的稀磷酸、濃度為４０％的氫氟酸按質量比１∶０．３０～０．４３混合，將該混合物溶液滴加在需修復的普通陶瓷表面并停留１～２分鐘；（２）將濃度為４０％的氫氟酸與氧化鋁粉末按質量比１∶０．７５混合，攪拌均勻，得到白色膏狀物，將其添加到經稀磷酸和氫氟酸處理過的陶瓷表面，經５～１０小時待膏體完全凝固后，拋光，陶瓷表面的損傷即可得到修復。
【技術特征摘要】
還沒有人留言評論。發表了對其他瀏覽者有用的留言會獲得科技券。