本發(fā)明專利技術(shù)涉及一種環(huán)保型高強鐵口樹脂套泥及鐵口泥套的制備方法，其特征在于：鐵口套泥是以熱固型酚醛樹脂樹脂為粘合劑，以剛玉顆粒為骨料，以剛玉粉、粘土粉、石墨粉、三氧化二鋁超微粉為粉料組成。制備鐵口泥套預(yù)制成型：按原料的重量組分取剛玉顆粒加入５０％量的熱固型酚醛樹脂粘合劑進(jìn)行攪拌，然后再加入剛玉粉、粘土粉、石墨粉、三氧化二鋁超微粉和另外５０％量的熱固型酚醛樹脂進(jìn)行攪拌，充分?jǐn)嚢韬蟪隽涎b模，振動成型。封裝：成型后用塑料薄膜風(fēng)裝，便于現(xiàn)場使用、長途運輸、長期保存。本發(fā)明專利技術(shù)明顯提高了鐵口泥套的產(chǎn)品質(zhì)量，同時縮短了制作時間、大大地減輕了工人的勞動強度，還具有節(jié)省原材料、降低成本、提高鐵口泥套的使用壽命的特點。

Method for preparing environment-friendly high-strength taphole resin liner and iron mouth mud sleeve

The invention relates to an environment-friendly high-strength iron resin clay and iron mouth mud set preparation method, which is characterized in that the iron muzzle mud is thermosetting phenolic resin as adhesive with corundum as aggregate, using corundum powder, clay powder, graphite powder, three two aluminum oxide ultrafine powder material composition. Preparation of iron mouth mud preformed: thermosetting phenolic resin adhesive with 50% by weight of the composition of raw material corundum particles to mix, then add the thermosetting phenolic resin corundum powder, clay powder, graphite powder, three two aluminum oxide superfine powder and the other 50% were stirring, stirring up material filling, vibration molding. Packaging: after molding, it is packed with plastic film, which is convenient for field use, long distance transportation and long term preservation. The invention improves the iron notch mud suite of product quality, and shorten the time of production, greatly reduce the labor intensity of the workers, but also has the characteristics of saving raw materials, reduce the cost and improve the service life of taphole mud.

【技術(shù)實現(xiàn)步驟摘要】

【技術(shù)保護(hù)點】
一種環(huán)保型高強鐵口樹脂套泥，其特征在于：環(huán)保型高強鐵口樹脂套泥是以樹脂為粘合劑，以剛玉顆粒為骨料，以剛玉粉、粘土粉、石墨粉、三氧化二鋁超微粉為粉料組成，其原料的重量組分是：熱固型酚醛樹脂１－２０份、剛玉顆粒５５－６２份、粉料的總量３５－４５份，其中：剛玉粉２０－２５份、粘土粉２－４份、石墨粉６－９份、三氧化二鋁超微粉３－６份。

【技術(shù)特征摘要】

【專利技術(shù)屬性】
技術(shù)研發(fā)人員：柴立峰，
申請(專利權(quán))人：柴立峰，
類型：發(fā)明
國別省市：21[中國|遼寧]