The invention discloses a preparation method of a polypropylene organic composite nucleating agent, which is composed of a Sorbitol Nucleating Agent and 1,3,5- benzene three formic acid () (BTCA-TCHA), and the proportion is 7:3~3:7. The invention uses Sorbitol Nucleating Agent and 1,3,5- benzene three formic acid three (cyclohexylamine) nucleation, has a great improvement on the crystallization behavior and mechanical properties of polypropylene and transparency, and because of the synergy between the two, reduce the two kinds of nucleating agent effective usage. The two kinds of nucleating agents were dissolved in N, N-, and methyl formamide in a proportion of, and then mixed with 3~5min at high speed. The invention has simple operation process and can be used for industrial production.
【技術實現步驟摘要】
本專利技術涉及一種聚丙烯成核劑的制備方法，具體涉及一種有機復合成核劑的制備方法，屬于復合材料領域。
技術介紹
聚丙烯作為五大通用塑料中發展最快的品種，具有原料來源豐富、價格較低、易于加工成型、產品性能優良等優點，故而具有非常廣泛的用途。但聚丙烯也存在一些不足之處（抗沖擊性差、高溫剛性不足、透明性差等），為了擴大聚丙烯的應用領域，延長其使用壽命，就必須對聚丙烯進行改性。現有對聚丙烯改性效果最好的是成核劑改性，添加成核劑可以改變聚丙烯的結晶特性，從而影響其物理機械性能。二亞芐基山梨醇類成核劑是目前應用最廣泛的成核劑，其中1,3:2,4-二亞芐基山梨醇（DBS）、1,3:2,4-二（對甲基亞芐基）山梨醇（MDBS）、1,3:2,4-二（3,4-二甲基亞芐基）山梨醇（DMDBS）分別為第一、二、三代山梨醇類成核劑，這類成核劑成核效果好，對聚丙烯透明性能改善尤為明顯，但是MDBS、DMDBS熔點一般較高，會影響其在聚丙烯中的分散性，且成本較高。成核劑1,3,5-苯三甲酸三(環己胺)對聚丙烯熱性能和力學性能有著明顯的提高，尤其對剛性的改善突出，但是對聚丙烯透明性的改善不如山梨醇類成核劑。將1,3,5-苯三甲酸三(環己胺)與山梨醇類成核劑按照比例配成復合成核劑，可以減少二者的有效使用量，使成本降低，對聚丙烯的力學性能和透明性有著更大的提高，且操作工藝簡單，可用于工業化生產。
技術實現思路
本專利技術提供了一種聚丙烯用有機復合成核劑的制備方法，該成核劑由山梨醇類成核劑與1,3,5-苯三甲酸三(環己胺)(BTCA-TCH...
【技術保護點】
一種聚丙烯有機復合成核劑的制備方法，其特征在于，所述復合成核劑由山梨醇類成核劑與1,3,5?苯三甲酸三(?環己胺)?(?BTCA?TCHA)組成，該復合成核劑由以下步驟合成：取山梨醇類成核劑和?1,3,5?苯三甲酸三(環己胺)?(BTCA?TCHA)，按照一定的重量比溶于入N,N?二甲基甲酰胺（DMF），在高速攪拌下攪拌3~5min，即得到目標成核劑。
【技術特征摘要】
1.一種聚丙烯有機復合成核劑的制備方法，其特征在于，所述復合成核劑由山梨醇類成核劑與1,3,5-苯三甲酸三(環己胺)(BTCA-TCHA)組成，該復合成核劑由以下步驟合成：取山梨醇類成核劑和1,3,5-苯三甲酸三(環己胺)(BTCA-TCHA)，按照一定的重量比溶于入N,N-二甲基甲酰胺（DMF），在高速攪拌下攪拌3~5min，即得到目標成核劑。
2.根據權利要求1所述的一種聚丙烯有機復合成...