The invention discloses a nanometer titanium dioxide coated modified calcium carbonate powder, the invention will be modified by stearic acid nano titanium dioxide in situ modification of calcium carbonate powder surface, and with titanate coupling agent as bridging agent, allows the production of nano titanium dioxide can firmly in calcium carbonate surface film, modified carbonate the calcium powder obtained has the unique optical properties of nano titanium dioxide, nano titanium dioxide powder can replace the expensive body, and the calcium carbonate modified after having good dispersion and suspension of nanometer titanium dioxide powder do not have, in the filling system has good dispersion effect, achieve excellent modification effect.
【技術實現步驟摘要】
本專利技術涉及無機粉體表面改性
，尤其涉及一種納米二氧化鈦包覆的改性碳酸鈣粉體及其制備方法。
技術介紹
碳酸鈣是一種十分常見的無機粉末填料，其價格低廉、無毒無味、白度高、硬度好等優點，在橡膠制品、造紙、油墨、塑料、涂料等等領域均有廣泛的應用，然而，碳酸鈣本質上一種無機礦物質，與有機物質親和相容性較差，直接填充將會導致產品性能嚴重劣化，使用范圍嚴重受限，因此，在實際應用中需要對碳酸鈣粉體進行改性處理。目前主要的改性方法有機械細化法、表面改性劑如偶聯劑、脂肪酸及其鹽、表面活性劑等改性兩大類，兩種方法各有其優勢，改性后的碳酸鈣性能也得到一定的改善。《硬脂酸-鈦酸酯偶聯劑改性重質碳酸鈣粉體研究》一文以硬脂酸、鈦酸酯偶聯劑作為復合改性劑，無水乙醇作為分散劑，采用濕法球磨對粉體進行改性處理，取得了較為理想的改性效果，但是這種方法制備得到的產品為疏水性產品，在水性油墨、水性涂料領域應用受到限制，且附加功能不足，僅限于補強增韌用，需要做進一步的改性處理，以擴寬其使用范圍。
技術實現思路
本專利技術目的就是為了彌補已有技術的缺陷，提供一種納米二氧化鈦包覆的改性碳酸鈣粉體及其制備方法。本專利技術是通過以下技術方案實現的：一種納米二氧化鈦包覆的改性碳酸鈣粉體，該改性碳酸鈣粉體由以下重量份的原料制成：碳酸鈣50、硬脂酸2-3、鈦酸四丁酯4-5、鈦酸酯偶聯劑2-3、無水乙醇60-80、環己烷10-15、三乙胺15-20、氨水適量。所述的一種納米二氧化鈦包覆的改性碳酸鈣粉體的制備方法包括以下步驟：（1）先將環己烷和三乙胺混合配制成溶液，隨后投入鈦酸四丁酯、硬脂酸，攪拌混合20-3...
【技術保護點】
一種納米二氧化鈦包覆的改性碳酸鈣粉體，其特征在于，該改性碳酸鈣粉體由以下重量份的原料制成：碳酸鈣50、硬脂酸2?3、鈦酸四丁酯4?5、鈦酸酯偶聯劑2?3、無水乙醇60?80、環己烷10?15、三乙胺15?20、氨水適量。
【技術特征摘要】
1.一種納米二氧化鈦包覆的改性碳酸鈣粉體，其特征在于，該改性碳酸鈣粉體由以下重量份的原料制成：碳酸鈣50、硬脂酸2-3、鈦酸四丁酯4-5、鈦酸酯偶聯劑2-3、無水乙醇60-80、環己烷10-15、三乙胺15-20、氨水適量。2.如權利要求1所述的一種納米二氧化鈦包覆的改性碳酸鈣粉體的制備方法，其特征在于，其制備方法包括以下步驟：（1）先將環己烷和三乙胺...
【專利技術屬性】
技術研發人員：陳永忠，
申請(專利權)人：青陽縣永誠鈣業有限責任公司，
類型：發明
國別省市：安徽;34
還沒有人留言評論。發表了對其他瀏覽者有用的留言會獲得科技券。