The invention discloses a method for preparing an adsorption of cobalt and copper beta naphthol modified activated carbon. (1) 50 80 DEG C temperature range, the beta naphthol dissolved in mass percentage concentration of 1 5% ethanol or sodium hydroxide solution, prepared into 0.1 beta naphthol 1mol/L mixed solution; (2) the 5 10g activated carbon into the 100mL step (1) mixed solution prepared in 10, immersion for 24 hours, and then filtered supernatant after drying, modified activated carbon preparation completed. The activated carbon prepared by the invention is a kind of special adsorbents to cobalt, copper ion adsorption and removal, simple preparation process, low cost, highly selective in the solution of copper or cobalt ion adsorption and removal, removal of cobalt ions can reach the limit below 0.5mg/L, copper ion limit below 0.1mg/L.
【技術實現步驟摘要】
吸附鈷、銅離子的β-萘酚改性活性炭的制備方法
本專利技術涉及活性炭的改性和制備方法，特別是針對鈷、銅離子的吸附、脫除用活性炭的開發利用。
技術介紹
活性炭作為一種吸附及催化材料,已在化工、石油、輕工、食品、環境保護、國防等諸多領域得到廣泛應用。在環境保護、有色金屬冶金、資源綜合利用等領域的應用主要以活性炭對重金屬離子的吸附性能為主要表現。在有色金屬冶金和資源綜合利用中，活性炭在低濃度溶液可以有效地對目標元素實施富集，在多元素共存溶液里能夠吸附雜質離子實現除雜凈化作用，因此活性炭已成為一些行業中特效的吸附劑或脫雜劑。大量的活性炭性質研究中發現，活性炭內部具有大量的官能團或基團，活性炭所表現出的一些催化或吸附性能取決于內在官能團或基團的性質，因此活性炭的改性或修飾研究方興未艾，針對某種功能應用要求，可以有的放矢地對活性炭進行改性，從而實現活性炭對某些性能要求的目標。
技術實現思路
本專利技術的目的是為了制備一種高效選擇性強的吸附用活性炭復合材料，通過添加活性劑的改性方法，制備出所需的活性炭。可以專門有效的吸附低濃度或多元素離子共存溶液中的銅、鈷有價金屬離子，是一種在環境保護、濕法冶金和資源綜合利用領域具有高效、選擇性強的吸附劑和除雜劑。具體步驟為：（1）50℃-80℃溫度范圍中，將β-萘酚溶于質量百分比濃度為1-5%的乙醇或氫氧化鈉溶液中，配制成0.1-1mol/Lβ-萘酚混合溶液。（2）稱取5-10g活性炭放入100mL步驟（1）所配制的混合溶液中,浸漬10-24小時，然后濾去清液后烘干，改性活性炭制取完成。（3）量取100mL濃度為0.5g/L的硫酸銅或硫酸鈷...
【技術保護點】
一種吸附鈷、銅離子的β?萘酚改性活性炭的制備方法，其特征在于具體步驟為：（1）50℃?80℃溫度范圍中，將β?萘酚溶于質量百分比濃度為1?5%的乙醇或氫氧化鈉溶液中，配制成0.1?1mol/Lβ?萘酚混合溶液；（2）稱取5?10g活性炭放入100mL步驟（1）所配制的混合溶液中,?浸漬10?24小時，然后濾去清液后烘干，改性活性炭制取完成。
【技術特征摘要】
1.一種吸附鈷、銅離子的β-萘酚改性活性炭的制備方法，其特征在于具體步驟為：（1）50℃-80℃溫度范圍中，將β-萘酚溶于質量百分比濃度為1-5%的乙醇或氫氧化鈉溶液中，配...
【專利技術屬性】
技術研發人員：李義兵，廖貴朗，劉家輝，鄭繼明，陸鳳嬌，李玉平，
申請(專利權)人：桂林理工大學，
類型：發明
國別省市：廣西,45