Preparation method of polyvinyl alcohol coating of the invention discloses a method for photographic paper, which comprises the following steps: (1) according to the weight ratio of 10 11:1 prepared water and polyvinyl alcohol as raw material; (2) adding water mixer, turn on the blender to stir; (3) adding polyvinyl alcohol, stirring for 5 minutes, to make it fully dispersed in water instead of agglomerating; (4) steam heating to 85 95 DEG C, and to maintain the temperature, stirring until completely dissolved 60min raw materials; (5) to stop steam heating, let the solution of natural cooling to 40 DEG C, i.e.. The invention provides a preparation method of polyvinyl alcohol paint used for photographic paper. The method has simple steps and good dispersibility of polyvinyl alcohol paint.
【技術實現步驟摘要】
一種應用于相紙的聚乙烯醇涂料的配制方法
本專利技術涉及紙業加工領域，具體為一種應用于相紙的聚乙烯醇涂料的配制方法。
技術介紹
適用于廣告、影像制作包括噴墨打印所使用的相紙原紙結構包括由純木漿制備成的、具有白度高、平滑度高和表觀細膩度高且無塵埃點的基材和設置于其一面或兩面的PE膜和吸墨成像層構成。其中所述的吸墨成像層由納米級三氧化二鋁粉末層構成或通過水溶性的聚乙烯醇(PVA)材料構成，由于聚乙烯醇是一種無毒并且容易分解的材料，因此被廣泛應用。
技術實現思路
為解決
技術介紹
提到的問題，本專利技術提出如下技術方案：一種應用于相紙的聚乙烯醇涂料的配制方法，包括如下步驟：(1)按照重量比為10-11:1準備水和聚乙烯醇原料；(2)將水加入攪拌器中，打開攪拌器開始攪拌；(3)加入聚乙烯醇，攪拌5分鐘，使其充分分散于水中而不是結塊成團；(4)蒸汽加熱至85-95℃，并維持此溫度，繼續攪拌60min，直至原料完全溶解；(5)停止蒸汽加熱，讓溶液自然冷卻至40℃，即得。進一步的，步驟(5)的冷卻過程中，每間隔4h攪拌一次，每次2min。本專利技術提出的一種應用于相紙的聚乙烯醇涂料的配制方法，步驟簡單，制得的聚乙烯醇涂料分散性好。具體實施方式：為了使本領域的技術人員更好地理解本專利技術的技術方案，下面對本專利技術作進一步說明：一種應用于相紙的聚乙烯醇涂料的配制方法，一種應用于相紙的聚乙烯醇涂料的配制方法，包括如下步驟：(1)按照重量比為10-11:1準備水和聚乙烯醇原料；(2)將水加入攪拌器中，打開攪拌器開始攪拌；(3)加入聚乙烯醇，攪拌5分鐘，使其充分分散于水中而不是結塊成團；...
【技術保護點】
一種打印紙加工中的聚乙烯醇原料的配制方法，包括如下步驟：(1)按照重量比為10?11:1準備水和聚乙烯醇原料；(2)將水加入攪拌器中，打開攪拌器開始攪拌；(3)加入聚乙烯醇，攪拌5分鐘，使其充分分散于水中而不是結塊成團；(4)蒸汽加熱至85?95℃，并維持此溫度，繼續攪拌60min，直至原料完全溶解；(5)停止蒸汽加熱，讓溶液自然冷卻至40℃，即得。
【技術特征摘要】
1.一種打印紙加工中的聚乙烯醇原料的配制方法，包括如下步驟：(1)按照重量比為10-11:1準備水和聚乙烯醇原料；(2)將水加入攪拌器中，打開攪拌器開始攪拌；(3)加入聚乙烯醇，攪拌5分鐘，使其充分分散于水中而不是結塊成團；(4)蒸汽加熱至85-...