The method of the invention relates to the field of thin slab continuous casting weather resistant steel, in particular to a method for producing a delayed casting steel of thin slab continuous casting. The method can improve the cooling strength of the slab by changing the nozzle height of the caster number section. In addition, the method of using mold bare copper (i.e. without coating) to produce resistant steel, this method can meet the needs of thin slab continuous casting production, at the same time, it is helpful to reduce the defects of longitudinal crack and improve the quality of slab. The inventive method for forming billet initial solidified shell from the control and cast two times the cooling intensity of billet, avoid the formation of small cracks expand point of technology, creatively developed new methods of resistance Hou steel production process to meet quality, Bo Banzhu machine production of corten steel needs.
【技術實現步驟摘要】
一種薄板坯連鑄的耐侯鋼生產方法
本專利技術方法涉及薄板坯連鑄耐侯鋼領域，具體為一種薄板坯連鑄的耐侯鋼生產方法。
技術介紹
薄板坯連鑄耐侯鋼SPA-H的成份設計中，[C]含量控制在0.04％～0.06％(不同于常規鑄機)，接近薄板坯鑄機包晶鋼碳含量0.07％～0.15％的范圍，屬于裂紋敏感性鋼種，易產生表面縱裂等質量缺陷。該鋼種的常規生產方式為鋼水在鍍層結晶器內冷卻成形，經扇形段噴淋二次冷卻后形成鑄坯。在帶有鍍層的結晶器銅板渣線處，由于鍍層的脫落與磨損，在初生的坯殼上形成細小的裂紋，因其薄板坯鑄機結晶器是漏斗型的特殊形式，在接近包晶區的鋼水發生包晶反應產生體積收縮時，更易使坯殼與銅板過早的脫離產生氣隙而形成細小的縱裂紋。細小縱裂紋出結晶器后在二次冷卻區繼續擴大，嚴重時會發生漏鋼。此種常規方法生產的耐侯鋼，已不能滿足薄板坯鑄機生產的需要及產品質量的需要。
技術實現思路
本專利技術的目的在于提供一種薄板坯連鑄的耐侯鋼生產方法，以滿足薄板鑄機生產及產品質量的要求，改善產品質量。本專利技術的技術方案是：一種薄板坯連鑄的耐侯鋼生產方法，調整鑄機扇形段冷卻噴嘴高度，使用無鍍層結晶器銅板，具體如下：①結晶器銅板上沿往下80～120mm處不進行鍍層，即裸銅；②調整鑄機零號扇形段內弧的冷卻噴嘴，使冷卻噴嘴提高60～100mm。本專利技術的優點及有益效果是：1、本專利技術方法通過改變提高鑄機零號扇形段噴嘴高度，從而降低鑄坯冷卻強度及采用結晶器裸銅(即無鍍層)的方法來生產耐侯鋼，此方法可以滿足薄板坯連鑄生產需要，同時有利于減少縱裂缺陷、提高鑄坯質量。2、本專利技術方法從控制鑄坯初始坯...
【技術保護點】
一種薄板坯連鑄的耐侯鋼生產方法，其特征在于，調整鑄機扇形段冷卻噴嘴高度，使用無鍍層結晶器銅板，具體如下：①結晶器銅板上沿往下80～120mm處不進行鍍層，即裸銅；②調整鑄機零號扇形段內弧的冷卻噴嘴，使冷卻噴嘴提高60～100mm。
【技術特征摘要】
1.一種薄板坯連鑄的耐侯鋼生產方法，其特征在于，調整鑄機扇形段冷卻噴嘴高度，使用無鍍層結晶器銅板，具體如下：①結晶器...
【專利技術屬性】
技術研發人員：劉軍，于華財，段富春，佟亞男，高沖，
申請(專利權)人：本鋼板材股份有限公司，
類型：發明
國別省市：遼寧,21