The invention discloses a preparation process of molybdenum alloy powder, the molybdenum alloy powder preparation process comprises the following steps: A, using a cationic membrane double chamber for electrolysis of sodium molybdate solution, separating sodium ion; B, the product of electrolytic anode chamber after cleaning and filtration to obtain filter cake; C, the filter cake is heated and dried in hydrogen reduction environment to obtain ferromolybdenum alloy powder. The invention relates to a preparation process of molybdenum alloy powder, prepared by electrolysis of molybdenum alloy powder with uniform particle size and high purity, not only greatly improve the quality of molybdenum alloy powder products, but also can effectively avoid the environmental pollution in the production process, and the process of low energy consumption, is conducive to energy saving and emission reduction.
【技術實現步驟摘要】
一種鉬鐵合金粉末制備工藝
本專利技術涉及一種合金粉末制備工藝，特別是涉及一種鉬鐵合金粉末制備工藝。
技術介紹
鉬鐵是鉬與鐵的合金，是重要的冶金添加劑，用量非常大。目前主要是采用鋁熱反應法來進行制備。但其制備過程中會產生大量的高溫含塵煙氣，不僅后續處理工藝復雜，而且所需設備復雜，處理成本高。
技術實現思路
本專利技術所要解決的技術問題是提供一種工藝溫度低、產品質量好的鉬鐵合金粉末制備工藝。為了解決上述技術問題，本專利技術采用如下技術方案：一種鉬鐵合金粉末制備工藝，包括以下步驟：A、采用具有陽離子膜的雙室電解槽對鉬酸鈉溶液進行電解，分離出鈉離子；B、將電解后的陽極室產物進行清洗并過濾得到濾餅；C、將濾餅加熱干燥后在氫氣環境下進行還原即得到鉬鐵合金粉末。作為優選，所述步驟A中電解槽陽極為鐵片，陰極為惰性電極，陽離子膜為全氟磺酸陽離子交換膜。作為優選，所述步驟B中用去離子水進行清洗。作為優選，所述步驟C中還原溫度為700-900攝氏度。與現有技術相比，本專利技術一種鉬鐵合金粉末制備工藝，通過電解法制得的鉬鐵合金粉末粒徑均勻且純度高，不僅大大的提高了鉬鐵合金粉產品品質，而且有效的避免了生產過程中的環境污染，同時工藝能耗低，有利于節能減排。具體實施方式本說明書中公開的所有特征，或公開的所有方法或過程中的步驟，除了互相排斥的特征和/或步驟以外，均可以以任何方式組合。本說明書中公開的任一特征，除非特別敘述，均可被其他等效或具有類似目的的替代特征加以替換。即，除非特別敘述，每個特征只是一系列等效或類似特征中的一個例子而已。實施例1：本專利技術一種鉬鐵合金粉末制備工藝，包括以下步...
【技術保護點】
一種鉬鐵合金粉末制備工藝，其特征在于，包括以下步驟：A、采用具有陽離子膜的雙室電解槽對鉬酸鈉溶液進行電解，分離出鈉離子；B、將電解后的陽極室產物進行清洗并過濾得到濾餅；C、將濾餅加熱干燥后在氫氣環境下進行還原即得到鉬鐵合金粉末。
【技術特征摘要】
1.一種鉬鐵合金粉末制備工藝，其特征在于，包括以下步驟：A、采用具有陽離子膜的雙室電解槽對鉬酸鈉溶液進行電解，分離出鈉離子；B、將電解后的陽極室產物進行清洗并過濾得到濾餅；C、將濾餅加熱干燥后在氫氣環境下進行還原即得到鉬鐵合金粉末。2.根據權利要求1所述的一種鉬鐵合金粉末制備工藝，其特...
【專利技術屬性】
技術研發人員：李成，
申請(專利權)人：四川省東宇信息技術有限責任公司，
類型：發明
國別省市：四川,51