The present invention relates to a new method for gas nitriding in a rotary furnace for a minimal workpiece, relating to a gas nitriding process and apparatus for extremely small workpieces. Methods: A, the workpiece is installed and fixed on the rotary furnace, the furnace body rotation; B, the furnace heating, the heating temperature is 580 degrees, the holding time is 30 minutes to 3 hours; C, when the temperature reaches 580 degrees when other gases NH3 or can produce nitrogen gas, exhaust gas flow a way to pass into the overflow of ammonia gas can be ignited. The invention has the advantages of novel structure, simple and advanced technology, improve productivity, uniform nitriding characteristics, a new method which belongs to a new set of economic and practical for small workpiece in rotary furnace gas nitriding.
【技術實現步驟摘要】
本專利技術所述的對于極小工件在回轉式爐中氣體滲氮的新方法，涉及一種極小型工件的氣體滲氮工藝及設備。
技術介紹
傳統的氣體氮化是在井式爐或多用爐中進行。對于大、中型零件能保證產品質量和生產率。但對于極小零件，外徑在10mm以內，厚度在2mm以內的工件就需要工裝夾具來協助完成滲氮工藝，但這樣的做法使得工藝夾具的用量極大，并且還不能保證極小工件滲氮層均勻一致，導致生產率大大降低。針對上述現有技術中所存在的問題，研究設計一種新型的對于極小工件在回轉式爐中氣體滲氮的新方法，從而克服現有技術中所存在的問題是十分必要的。
技術實現思路
鑒于上述現有技術中所存在的問題，本專利技術的目的是研究設計一種新型的對于極小工件在回轉式爐中氣體滲氮的新方法。用以解決現有技術中存在的：1、工藝夾具用量極大；2、不能保證極小工件滲氮均勻；3、生產率降低等問題。本專利技術的技術解決方案是這樣實現的：本專利技術所述的對于極小工件在回轉式爐中氣體滲氮的新方法；其方法為：a、將工件裝于回轉式爐內并固定，使爐體旋轉；b、對爐體進行加熱，加熱溫度為520-580度；c、當溫度達到520-580度時通入氨氣或能夠產生氮氣的其他氣體，通入氨氣的流量一路內溢出的廢氣能夠點燃即可；本專利技術所述的加熱溫度為520-580度，保溫時間為30分鐘至3小時。本專利技術的優點是顯而易見的，主要表現在：本專利技術不但不需要工裝夾具，而且因...
【技術保護點】
一種對于極小工件在回轉式爐中氣體滲氮的新方法；其方法為：a、將工件裝于回轉式爐內并固定，使爐體旋轉；b、對爐體進行加熱，加熱溫度為520?580度；c、當溫度達到520?580度時通入氨氣或能夠產生氮氣的其他氣體，通入氨氣的流量一路內溢出的廢氣能夠點燃即可。
【技術特征摘要】
1.一種對于極小工件在回轉式爐中氣體滲氮的新方法；其方法為：
a、將工件裝于回轉式爐內并固定，使爐體旋轉；
b、對爐體進行加熱，加熱溫度為520-580度；
c、當溫度達到520-580度時通入氨氣或能夠產生氮...