The invention discloses a molding method for the decorative painting of crystal elements, which comprises the following steps: first, the positive and negative sides of the base material are sanded and worn to make the two sides of the substrate smooth and smooth and smeared with the paint, and then the base material is drilled, the pattern is engraved with the numerical control equipment, and then the epoxy resin sealing glue is used to seal the base material. Glue treatment, then select the high quality shell, carve the pattern on the shell and stick the carve shell with glue on the base material, then take the crystal inlaid on the substrate and fix it. Finally, the epoxy resin seal is used to seal the whole base material again, and the wind is dry for 24 hours at normal temperature. The invention adopts the crystal inlaid on the base material and sticky the shell of various patterns on the surface of the base material. The whole operation process is simple because it is implemented, the product shape is rich and beautiful, which conforms to the aesthetic concept of the existing consumers, and has a very high market value.
【技術(shù)實(shí)現(xiàn)步驟摘要】
一種水晶元素裝飾畫成型方法
本專利技術(shù)屬于掛畫生產(chǎn)制造領(lǐng)域，特別是涉及一種水晶元素裝飾畫成型方法。
技術(shù)介紹
隨著家居裝修行業(yè)的興起，人們對(duì)室內(nèi)裝潢設(shè)計(jì)的樣式越來越重視，掛畫裝飾作為裝潢中主要的一部分，也需要迎合消費(fèi)者需求?，F(xiàn)有市場(chǎng)中出現(xiàn)的掛畫，大多樣式單一，款式缺乏新穎，越來越滿足不了市場(chǎng)需求，因此如何解決上述問題成為本領(lǐng)域研究人員亟需解決的難題。
技術(shù)實(shí)現(xiàn)思路
本專利技術(shù)的目的就是提供一種一種水晶元素裝飾畫成型方法，能完全解決上述現(xiàn)有技術(shù)的不足之處。本專利技術(shù)的目的通過下述技術(shù)方案來實(shí)現(xiàn)：一種水晶元素裝飾畫成型方法，包括以下步驟：1）將基材的正反兩面砂光并打磨使基材正反兩面平整光滑；2）將基材的正反兩面均勻涂刷油漆，并用流平機(jī)流平；3）對(duì)照?qǐng)D紙，運(yùn)用數(shù)控設(shè)備對(duì)基材鉆孔，雕刻花紋；4）使用環(huán)氧樹脂封膠對(duì)基材進(jìn)行封膠處理；5）選取優(yōu)質(zhì)貝殼，在貝殼上雕刻圖案并將雕刻好圖案的貝殼用膠水粘黏在基材上；6）取水晶鑲嵌于基材上的孔內(nèi)固定；7）使用環(huán)氧樹脂封膠對(duì)整個(gè)基材再次封膠，并在常溫下風(fēng)干24小時(shí)。作為優(yōu)選，所述基材采用實(shí)木制成。作為優(yōu)選，步驟2）中采用滾輪涂抹的方式涂刷油漆。作為優(yōu)選，步驟2）中使用的油漆為水性漆。作為優(yōu)選，步驟3）中數(shù)控設(shè)備的主軸轉(zhuǎn)速為2000r/min-2200r/min。作為優(yōu)選，步驟4）和7）使用的環(huán)氧樹脂封膠中環(huán)氧樹脂和膠水體積比為3∶1。作為優(yōu)選，步驟4）中封膠處理后的環(huán)氧樹脂封膠厚度為1mm-2mm。與現(xiàn)有技術(shù)相比，本專利技術(shù)的有益效果在于：本專利技術(shù)結(jié)構(gòu)簡單，設(shè)計(jì)合理，采用將水晶鑲嵌在基材上，并在基材表面粘黏各式雕刻花紋的貝殼，整個(gè)操...
【技術(shù)保護(hù)點(diǎn)】
一種水晶元素裝飾畫成型方法，其特征在于：包括以下步驟：1）將基材的正反兩面砂光并打磨使基材正反兩面平整光滑；2）將基材的正反兩面均勻涂刷油漆，并用流平機(jī)流平；3）對(duì)照?qǐng)D紙，運(yùn)用數(shù)控設(shè)備對(duì)基材鉆孔，雕刻花紋；4）使用環(huán)氧樹脂封膠對(duì)基材進(jìn)行封膠處理；5）選取優(yōu)質(zhì)貝殼，在貝殼上雕刻圖案并將雕刻好圖案的貝殼用膠水粘黏在基材上；6）取水晶鑲嵌于基材上的孔內(nèi)固定；7）使用環(huán)氧樹脂封膠對(duì)整個(gè)基材再次封膠，并在常溫下風(fēng)干24小時(shí)。
【技術(shù)特征摘要】
1.一種水晶元素裝飾畫成型方法，其特征在于：包括以下步驟：1）將基材的正反兩面砂光并打磨使基材正反兩面平整光滑；2）將基材的正反兩面均勻涂刷油漆，并用流平機(jī)流平；3）對(duì)照?qǐng)D紙，運(yùn)用數(shù)控設(shè)備對(duì)基材鉆孔，雕刻花紋；4）使用環(huán)氧樹脂封膠對(duì)基材進(jìn)行封膠處理；5）選取優(yōu)質(zhì)貝殼，在貝殼上雕刻圖案并將雕刻好圖案的貝殼用膠水粘黏在基材上；6）取水晶鑲嵌于基材上的孔內(nèi)固定；7）使用環(huán)氧樹脂封膠對(duì)整個(gè)基材再次封膠，并在常溫下風(fēng)干24小時(shí)。2.根據(jù)權(quán)利要求1所述的一種水晶元素裝飾畫成型方法，其特征在于：所述基材采用實(shí)木制成。3.根據(jù)權(quán)利要求1所述的一種水晶元...