The invention discloses an antioxidant powder coating, which is composed of the following weight components: high density polypropylene 110_130, mercaptobutyl tin 0.7_1, beta_hydroxyalkylamide 1_2, polyvinyl butyral 3_4, fatty acid polyethylene glycol ester 1_2, polyvinyl alcohol 4_5, microcrystalline paraffin 5_7, calcium naphthenate 0.5_1, polyvinyl acetal 3_4. Tert-butyl p-diphenyl phenol 0.7_1 and silicon powder 10_14. The invention firstly disperses silicon powder in aqueous solution of beta_hydroxyalkylamide, and then blends with amide solution of paraffin wax, which can effectively improve the dispersion compatibility between silicon powder and paraffin wax, thereby improving the uniform stability of finished product coating film.
【技術實現步驟摘要】
一種抗氧化粉末涂料及其制備方法
本專利技術屬于涂料領域，具體涉及一種抗氧化粉末涂料及其制備方法。
技術介紹
粉末涂料是一種新型的不含溶劑100%固體粉末狀涂料。具有不用溶劑、無污染、節省能源和資源、減輕勞動強度和涂膜機械強度高等特點。它有三大類：熱塑性粉末涂料（PE）、熱固性粉末涂料、建筑粉末涂料。涂料由特制樹脂、顏填料、固化劑及其它助劑，以一定的比例混合，再通過熱擠塑和粉碎過篩等工藝制備而成。它們在常溫下，貯存穩定，經靜電噴涂、摩擦噴涂（熱固方法）或流化床浸涂（熱塑方法），再加熱烘烤熔融固化，使形成平整光亮的永久性涂膜，達到裝飾和防腐蝕的目的。其特性有：1、該產品不含毒性，不含溶劑和不含揮發有毒性的物質，故無中毒、無火災、無“三廢”的排放等公害的問題，完全符合國家環保法的要求。2、原材料利用率高，一些知名品牌的粉末供應商生產的粉末，其過噴的粉末可回收利用，最高的利用率甚至能達99％以上。3、被涂物前處理后，一次性施工，無需底涂，即可得到足夠厚度的涂膜，易實現自動化操作，生產效率高，可降低成本。4、涂層致密、附著力、抗沖擊強度和韌性均好，邊角覆蓋率高，具有優良的耐化學藥品腐蝕性能和電氣絕緣性能。5、粉末涂料存貯、運輸安全和方便。然而隨著社會的發展，人們對于涂料的要求也越來越高，對于傳統粉末涂料的強度和穩定性等都提出了更高的要求。
技術實現思路
本專利技術的目的在于針對現有技術的缺陷和不足，提供一種抗氧化粉末涂料及其制備方法。為實現上述目的，本專利技術采用以下技術方案：一種抗氧化粉末涂料，它是由下述重量份的原料組成的：高密度聚丙烯110-130、硫醇丁基錫0.7...
【技術保護點】
1.一種抗氧化粉末涂料，其特征在于，它是由下述重量份的原料組成的：高密度聚丙烯110?130、硫醇丁基錫0.7?1、β?羥烷基酰胺1?2、聚乙烯醇縮丁醛3?4、脂肪酸聚乙二醇酯1?2、聚乙烯醇4?5、微晶石蠟5?7、環烷酸鈣0.5?1、叔丁基對二苯酚0.7?1、硅微粉10?14。
【技術特征摘要】
1.一種抗氧化粉末涂料，其特征在于，它是由下述重量份的原料組成的：高密度聚丙烯110-130、硫醇丁基錫0.7-1、β-羥烷基酰胺1-2、聚乙烯醇縮丁醛3-4、脂肪酸聚乙二醇酯1-2、聚乙烯醇4-5、微晶石蠟5-7、環烷酸鈣0.5-1、叔丁基對二苯酚0.7-1、硅微粉10-14。2.一種如權利要求1所述的抗氧化粉末涂料的制備方法，其特征在于，包括以下步驟：（1）取叔丁基對二苯酚，加入到其重量10-17倍的無水乙醇中，攪拌均勻，升高溫度為60-65℃，加入環烷酸鈣，保溫攪拌20-30分鐘，得醇溶液；（2）取β-羥烷基酰胺、硅微粉混合，加入到混合料重量26-30倍的去離子水中，超聲10-15分鐘，得...