The invention discloses a production process of sand-in-water granulating liquid, which comprises the following steps: 1) adding 744 weight water, 1.5 weight SD_5W and 250 weight 10% SD_08 into a reaction kettle, stirring at a rotating speed of 800_1000r/min for 5_10 minutes at 15_25 C to obtain mixed solution A; 2) and 2.5 weight K14 antiseptic. The agent, 0.5 and 1.5 parts of AMP_95 and 1.5 parts of film-forming additives were added to the mixture A and stirred for 5_10 minutes at a rotating speed of 400_500 r/min at 15_25 C. The mixture B was obtained; 3) and the mixture B was stationary for 2_3 hours. The granulating liquid prepared by the invention is used for sand-in-water coating, and the obtained coating has high simulation degree, and effectively solves the problems in the background technology.
【技術實現步驟摘要】
一種水包沙造粒液的生產工藝
本專利技術屬于涂料工藝領域，具體地說，涉及到一種水包沙造粒液的生產工藝。
技術介紹
涂料，在中國傳統名稱為油漆，所謂涂料是涂覆在被保護或被裝飾的物體表面，并能與被涂物形成牢固附著的連續薄膜，通常是以樹脂、或油、或乳液為主，添加或不添加顏料、填料，添加相應助劑，用有機溶劑或水配制而成的粘稠液體。目前，建筑裝飾涂料水性化已經成為必然的發展趨勢，然而采用水性涂料裝飾的建筑真石質感還比較差，其仿真度主要取決于造粒液的配方工藝。
技術實現思路
針對上述問題，本專利技術提供了一種水包沙造粒液的生產工藝，生產出來的造粒液用于水包沙涂料，得到的涂料具有較高的仿真度，從而有效解決
技術介紹
中指出的問題。本專利技術采用的技術方案是：一種水包沙造粒液的生產工藝，包括以下步驟：1)、將744重量份水、1.5重量份SD-5W解變劑和250重量份10％SD-08加入到反應釜中，在15-25℃下以800-1000r/min的轉速攪拌5-10分鐘，得到混合液A；2)、將2.5重量份k14防腐劑、0.5重量份AMP-95和1.5重量份成膜助劑加入到混合液A中，在15-25℃下以400-500r/min的轉速攪拌5-10分鐘，得到混合液B；3)、將混合液B靜置2-3小時，得到成品。本專利技術制得的造粒液用于水包沙涂料，得到的涂料具有較高的仿真度，有效解決了
技術介紹
中的問題。具體實施方式下面通過具體的實施例對本專利技術做進一步的詳細描述。實施例一種水包沙造粒液的生產工藝，包括以下步驟：1)、將744重量份水、1.5重量份SD-5W解變劑和250重量份10％SD-08加入到...
【技術保護點】
1.一種水包沙造粒液的生產工藝，其特征在于，包括以下步驟：1)、將744重量份水、1.5重量份SD?5W解變劑和250重量份10％SD?08加入到反應釜中，在15?25℃下以800?1000r/min的轉速攪拌5?10分鐘，得到混合液A；2)、將2.5重量份k14防腐劑、0.5重量份AMP?95和1.5重量份成膜助劑加入到混合液A中，在15?25℃下以400?500r/min的轉速攪拌5?10分鐘，得到混合液B；3)、將混合液B靜置2?3小時，得到成品。
【技術特征摘要】
1.一種水包沙造粒液的生產工藝，其特征在于，包括以下步驟：1)、將744重量份水、1.5重量份SD-5W解變劑和250重量份10％SD-08加入到反應釜中，在15-25℃下以800-1000r/min的轉速攪拌5-10分鐘，得到...
【專利技術屬性】
技術研發人員：李志強，
申請(專利權)人：浙江長興凱士涂料有限公司，
類型：發明
國別省市：浙江,33