The invention relates to a preparation method of Fischer-Tropsch wax crude product, belonging to the technical field of Fischer-Tropsch wax production. The preparation method of the invention comprises the following steps: (1) melting the black wax, mixing and decolorizing the white clay with a weight of 5 20% of the black wax, filtering, and obtaining Fischer-Tropsch wax with a melting point of 90 105 (?) melting the Fischer-Tropsch wax with a melting point of 90 105 (?) to obtain the liquid Fischer-Tropsch wax; and (3) evaporating, dewatering and pre-distillation of the liquid Fischer-Tropsch wax film obtained in step 2, and Product. The invention crudely purifies Fischer-Tropsch wax by clay decolorization reaction, filtration and film evaporation, and has the advantages of simple operation.
【技術實現步驟摘要】
一種費托蠟粗產品的制備方法
本專利技術涉及一種費托蠟粗產品的制備方法，屬于費托蠟生產
技術介紹
費托蠟是煤制氣通過費托合成制取的蠟，主要成分為C12-C90烷烴，正構烷烴含量達80％以上，熔點達90℃以上。由相對分子質量在200-1200的直鏈、飽和的高碳烷烴組成，具有精細的晶體結構、高熔點、低油含量、低針入度、低遷移率、低熔融粘度、堅硬、耐磨及穩定性高等優點。費托蠟主要用于熱熔膠、油墨及涂料、塑料加工(PVC潤滑劑、聚烯烴潤滑劑及色母粒料分散劑)等領域。費托蠟是EVA基熱熔膠所使用的理想合成蠟，高熔點的蠟能夠提高膠粘劑的耐熱性和快干性。當費托蠟以微粒狀粉末使用在油墨中，可以提高應用材料的耐磨性、抗皺性，應用在涂層時，可以起到起皺效果，在微粉狀態使用時能形成條紋和水紋起皺效果，在加入粉末涂料樹脂，在擠出過程中起潤滑作用，可降低螺桿扭矩，減少能耗提高生產效率。費托蠟與PVC加工用穩定劑協同效果明顯，可以有效延長熱穩定時間，增加工藝溫度的調節幅度，在CPVC樹脂加工時尤為明顯，由于CPVC樹脂加工工藝參數調節范圍窄增加了產品的加工難度，可有效改善CPVC產品加工的后期潤滑，提升產品的外觀以及力學性能。
技術實現思路
本專利技術通過對含有費托蠟和催化劑的黑蠟脫色、過濾、薄膜蒸發，得到費托蠟粗產品以作為高品質費托蠟產品的原料或其他用途。本專利技術提供了一種費托蠟粗產品的制備方法，所述制備方法包括如下步驟：①將黑蠟熔化，加入黑蠟重量5-20％的白土攪拌脫色，過濾，得到熔點為90-105℃的費托蠟；②將步驟①所得熔點為90-105℃的費托蠟熔化，得到液態費托蠟；...
【技術保護點】
1.一種費托蠟粗產品的制備方法，其特征在于：所述制備方法包括如下步驟：①將黑蠟熔化，加入黑蠟重量5?20％的白土攪拌脫色，過濾，得到熔點為90?105℃的費托蠟；②將步驟①所得熔點為90?105℃的費托蠟熔化，得到液態費托蠟；③將步驟②所得液態費托蠟薄膜蒸發，脫去水和前餾，得到費托蠟粗產品。
【技術特征摘要】
1.一種費托蠟粗產品的制備方法，其特征在于：所述制備方法包括如下步驟：①將黑蠟熔化，加入黑蠟重量5-20％的白土攪拌脫色，過濾，得到熔點為90-105℃的費托蠟；②將步驟①所得熔點為90-105℃的費托蠟熔化，得到液態費托蠟；③將步驟②所得液態費托蠟薄膜蒸發，脫去水和前餾，得到費托蠟粗產品。2.根據權利要求1所述費托蠟粗產品的制備方法，其特征在于：所述步驟①中黑蠟的熔化溫度為120-160℃。3.根據權利要求2所述費托蠟粗產品...
【專利技術屬性】
技術研發人員：劉新濤，
申請(專利權)人：大連隆星新材料有限公司，
類型：發明
國別省市：遼寧,21