The invention provides a preparation method of a water borne nano silicon resin compound. The waterborne nano silicon resin is prepared by using one or several siloxane, under the participation of nano oxide, under the catalyst initiation, the hydrolysis polycondensation reaction is made at normal temperature and atmospheric pressure. Another purpose of the present invention is to provide an industrial coating with superior properties such as thermal stability, abrasion resistance, non adhesion, easy cleaning and high strength, which is prepared by using such water-based nano silicon resin as a base material.
【技術實現(xiàn)步驟摘要】
本專利技術涉及和水性納米硅樹脂在工業(yè)涂料中的應用，屬于新材料領域。
技術介紹
目前國內(nèi)用于生產(chǎn)不粘鍋、電熨斗、排氣管、拉發(fā)器、各種塑料面板等涂料用的硅樹脂主要是油性有機硅樹脂。該類硅樹脂具有附著力好、硬度高、光澤度高、耐高溫等優(yōu)點， 作為增硬涂層和各類金屬制品、裝飾材料、石刻文物等的保護涂層用原材料，可以顯著提高涂層的耐磨(高硬度)、耐高溫、耐老化、耐腐蝕、耐水和抗紫外線等性能。但是，考證對人體無害的環(huán)保涂料的一個國家標準是涂料中可揮發(fā)性有機物含量(VOC)小于200克/升，而油性有機硅樹脂配制的涂料，卻需要大量有機溶劑，不僅在制備硅樹脂過程中達不到國標， 更在應用上嚴重超標。而不粘涂料用特氟龍PTFE(聚四氟乙烯)樹脂，雖然具有最高使用溫度^0-300°C， 極低的摩擦系數(shù)、良好的耐磨性以及極好的化學穩(wěn)定性，但是，用于制造特氟隆涂層的全氟辛酸銨在加熱到240攝氏度時會釋放出有毒微粒，這種微粒可在10分鐘內(nèi)對老鼠造成嚴重傷害，在更長時間內(nèi)足以讓老鼠斃命。美國環(huán)境保護局下屬科學顧問委員會2006年2月通過獨立專家審核小組評估報告，將特氟隆原料全氟辛酸銨的危險性從“潛在致癌”提高到 “可能致癌”。而杜邦等8家主要化工企業(yè)已宣布到2015年完全停產(chǎn)特氟隆。
技術實現(xiàn)思路
本專利技術的目的是提供一種水性納米硅樹脂的制備方法，以及該硅樹脂在工業(yè)涂料中的應用。本專利技術所述的水性納米硅樹脂是由多官能團有機硅單體經(jīng)水解、聚合反應而生成的無色透明的硅樹脂水溶液。本專利技術所述的水性納米硅樹脂是選用一種或幾種硅氧烷，在納米氧化物參與下， 在催化劑引發(fā)下，于常溫(25°C 士5...
【技術保護點】
１．一種水性納米硅樹脂化合物的制備方法，其特征在于：選用一種或幾種硅氧烷， 在納米氧化物參與下，在催化劑引發(fā)下，于常溫（２５℃±５℃）常壓下水解縮聚反應，從而制得無色透明硅樹脂水溶液。
【技術特征摘要】
【專利技術屬性】
技術研發(fā)人員：俞介兵，許俊杰，
申請(專利權(quán))人：黃山陽昕涂料有限公司，
類型：發(fā)明
國別省市：34
還沒有人留言評論。發(fā)表了對其他瀏覽者有用的留言會獲得科技券。